品名： PEI 牌号：2200 厂家：美国Tyne
规格用途| 规格级别 | 其它 其它 其它 | 外观颜色 | nan |
| 该料用途 | nan | ||
| 备注说明 | nan | ||
技术参数| 项目性能 | 性能子项 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|---|
| 基本性能 | 熔体流动速率 | nan | ASTM D-1238 | 5.3 | g/10min |
| 吸水率 | 平衡,73℉ | ASTM D-570 | 1.10 | % | |
| 吸水率 | 24小时，73℉ | ASTM D-570 | 0.190 | % | |
| 密度 | nan | ASTM D-1505 | 0.961 | g/cm3 | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 0.70 | g/10min | |
| 熔体流动速率 | 190℃/21.6kg | ASTM D-1238 | 50 | g/10min | |
| 热性能 | 热变形温度 | 66Psi | ASTM D-648 | 410 | ℉ |
| 维卡软化点 | nan | ASTM D-1525 | 428 | ℉ | |
| 热指数 | 电性能 | nan | UL746B | 170 | |
| 热指数 | 机械冲击性能 | nan | UL746B | 170 | |
| 热指数 | 非机械性能 | nan | UL746B | 170 | |
| 热变形温度 | 264Psi | ASTM D-648 | 408 | ℉ | |
| 燃烧性 | nan | UL 94 | V-0 | class | |
| 线膨胀系数 | flow | nan | ASTM E-831 | 1×10-5 | |
| 线膨胀系数 | xflow | nan | ASTM E-831 | - | |
| 维卡软化温度 | nan | ASTM D-1525 | 130 | ℃ | |
| 熔化温度 | nan | DSC | 133 | ℃ | |
| 结晶温度 | nan | ASTM D-3418 | 119 | ℃ | |
| 热变形温度 | 1.8 MPa, 未退火 | ISO 75-2/A | 125 | ℃ | |
| 维卡软化点 | ISO 306 | 145 | ℃ | ||
| 线形膨胀系数 - 流动 | ASTM D696 | 0.000065 | cm/cm/℃ | ||
| 阻燃等级 | 1.90 mm | UL 94 | HB | ||
| 阻燃等级 | 0.360 mm | UL 94 | V-2 | ||
| 热灯丝点火温度 | 3.00 mm | IEC 60695-2-13 | 850 | ||
| 维卡软化温度 | ISO 306/A, ASTM D1525 2 | < 40.0 | ℃ | ||
| 熔融温度 | ISO 11357-3 | 87.1 | ℃ | ||
| 热变形温度 | 1.8 MPa, 未退火 | ASTM D648 | 119 | ℃ | |
| UL 阻燃等级 | UL 94 | V-0 | |||
| 玻璃转化温度 | DSC | Internal Method | -24.0 | ℃ | |
| 维卡软化温度 | ASTM D1525 | 63.0 | ℃ | ||
| 溶融温度 | DSC | Internal Method | 82.2 | ℃ | |
| 电气性能 | 体积电阻率 | ASTM D257 | 1.0E+16 | ohm.cm | |
| 介电强度 | 3.18mm,in Air | ASTM D149 | 16 | kV/mm | |
| 介电常数 | 1 MHz | ASTM D150 | 2.90 | ||
| 耗散因数 | 1 MHz | ASTM D150 | 0.010 |