品名： PUR 牌号：Curene® 442 厂家：美国Anderson
规格用途| 规格级别 | 其它 其它 其它 | 外观颜色 | nan |
| 该料用途 | nan | ||
| 备注说明 | nan | ||
技术参数| 项目性能 | 性能子项 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|---|
| 基本性能 | 密度 | nan | ASTM D1505 | 1.16 | g/cm3 |
| 密度 | nan | ASTM D1505 | 1.22 | g/cm3 | |
| 吸水率 | nan | ASTM D955 | 1.4 | % | |
| 密度 | nan | ASTM D1505 | 1.07 | g/cm3 | |
| 吸水率 | nan | ASTM D955 | 1.3 | % | |
| 伸长率 | nan | ASTM D412 | 550 | % | |
| 密度 | nan | ASTM D1505 | 1.13 | g/cm3 | |
| 硬度 | nan | ASTM D2240 | 95 | nan | |
| 密度 | nan | ASTM D1505 | 1.14 | g/cm3 | |
| 吸水率 | nan | ASTM D995 | 1.1 | % | |
| 硬度 | nan | ASTM D2240 | 70 | nan | |
| 密度 | nan | ASTM D1505 | 1.08 | g/cm3 | |
| 密度 | nan | ASTM D1505 | 1.08 | g/cm3 | |
| 密度 | nan | ASTM D1505 | 1.16 | g/cm3 | |
| 密度 | nan | ASTM D1505 | 1.09 | g/cm3 | |
| 吸水率 | nan | ASTM D955 | 1.1 | % | |
| 密度 | nan | ASTM D1505 | 1.23 | g/cm3 | |
| 密度 | nan | ASTM D1505 | 1.16 | g/cm3 | |
| 密度 | nan | ASTM D1505 | 1.20 | g/cm3 | |
| 密度 | nan | ASTM D412 | 1.17 | g/cm3 | |
| 吸水率 | nan | ASTM D955 | 1.2 | % | |
| 密度 | nan | ASTM D1505 | 1.25 | g/cm3 | |
| 密度 | nan | ASTM D1505 | 1.18 | g/cm3 | |
| 密度 | nan | ASTM D1505 | 1.20 | g/cm3 | |
| 密度 | nan | ASTM D1505 | 1.23 | g/cm3 | |
| 吸水率 | nan | ASTM D955 | 1.3 | % | |
| 密度 | nan | ASTM D1505 | 1.19 | g/cm3 | |
| 密度 | nan | ASTM D1505 | 1.18 | g/cm3 | |
| 水溶性 | nan | ASTM D955 | 1.2 | % | |
| 机械性能 | 硬度 | nan | ASTM D2240 | 75 | nan |
| 拉伸系数 | nan | ASTM D412 | 38.6 | MPa | |
| 拉伸强度 | nan | ASTM D412 | 51.0 | MPa | |
| 伸长率 | nan | ASTM D412 | 260 | % | |
| 硬度 | nan | ASTM D2240 | 81 | nan | |
| 拉伸系数 | 100% Strain | ASTM D412 | 3.96 | MPa | |
| 拉伸系数 | 300% Strain | ASTM D412 | 6.00 | MPa | |
| 拉伸强度 | nan | ASTM D412 | 50.3 | MPa | |
| 伸长率 | nan | ASTM D412 | 640 | % | |
| 硬度 | nan | ASTM D2240 | 84 | nan | |
| 拉伸系数 | 100% Strain | ASTM D412 | 4.69 | MPa | |
| 拉伸系数 | 300% Strain | ASTM D412 | 8.27 | MPa | |
| 拉伸强度 | Yield | ASTM D412 | 31.7 | MPa | |
| 拉伸系数 | 100% Strain | ASTM D412 | 13..8 | MPa | |
| 拉伸系数 | 300% Strain | ASTM D412 | 29.3 | MPa | |
| 拉伸强度 | Yield | ASTM D412 | 51.0 | MPa | |
| 伸长率 | nan | ASTM D412 | 400 | % | |
| 硬度 | nan | ASTM D2240 | 61 | nan | |
| 拉伸系数 | 100% Strain | ASTM D412 | 21.1 | MPa | |
| 拉伸系数 | 300% Strain | ASTM D412 | 46.7 | MPa | |
| 拉伸强度 | Yield | ASTM D412 | 51.0 | MPa | |
| 伸长率 | nan | ASTM D412 | 310 | % | |
| 密度 | nan | ASTM D1505 | 1.16 | g/cm3 | |
| 拉伸系数 | 100% Strain | ASTM D412 | 26.5 | MPa | |
| 伸长率 | nan | ASTM D412 | 260 | % | |
| 拉伸强度 | Yield | ASTM D412 | 50.3 | MPa | |
| 硬度 | nan | ASTM D2240 | 90 | nan | |
| 压缩强度 | 10% Strain | ASTM D695 | 2.45 | MPa | |
| 压缩强度 | 5% Strain | ASTM D695 | 0.545 | MPa | |
| 压缩强度 | 15% Strain | ASTM D695 | 4.41 | MPa | |
| 压缩强度 | 25% Strain | ASTM D695 | 6.18 | MPa | |
| 拉伸系数 | 100% Strain | ASTM D412 | 7.69 | MPa | |
| 拉伸系数 | 300% Strain | ASTM D412 | 14.1 | MPa | |
| 拉伸强度 | Yield | ASTM D412 | 44.7 | MPa | |
| 断裂伸长率 | nan | ASTM D412 | 470 | % | |
| 硬度 | nan | ASTM D2240 | 92 | nan | |
| 压缩强度 | 5% Strain | ASTM D695 | 1.49 | MPa | |
| 压缩强度 | 10% Strain | ASTM D695 | 3.55 | MPa | |
| 压缩强度 | 15% Strain | ASTM D695 | 5.65 | MPa | |
| 压缩强度 | 25% Strain | ASTM D695 | 8.48 | MPa | |
| 拉伸系数 | 100% Strain | ASTM D412 | 10.0 | MPa | |
| 拉伸系数 | 300% Strain | ASTM D412 | 20.8 | MPa | |
| 拉伸强度 | Yield | ASTM D412 | 49.2 | MPa | |
| 断裂伸长率 | nan | ASTM D412 | 410 | % | |
| 硬度 | nan | ASTM D2240 | 92 | nan | |
| 拉伸系数 | 100% Strain | ASTM D412 | 8.89 | MPa | |
| 拉伸系数 | 300% Strain | ASTM D412 | 17.7 | MPa | |
| 拉伸强度 | Yield | ASTM D412 | 59.3 | MPa | |
| 断裂伸长率 | nan | ASTM D412 | 430 | % | |
| 硬度 | nan | ASTM D2240 | 95 | nan |