技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔融指数 |
200℃/5kg |
ISO 1133:1997 |
2.5 |
cm3/10min |
| 吸水率 |
nan |
ISO 62:1999 |
0.1 |
% |
| 电气性能 |
体积电阻率 |
|
ASTM D-257 |
1.0E+17 |
ohm·cm |
| 介电强度 |
|
ASTM D-149 |
15 |
kV/mm |
| 介电常数 |
50Hz |
ASTM D-150 |
3.0 |
|
| 介电常数 |
1MHz |
ASTM D-150 |
2.9 |
|
| 耗散因素 |
50Hz |
ASTM D-150 |
0.00090 |
|
| 耗散因素 |
1MHz |
ASTM D-150 |
0.010 |
|
| 耐电弧性 |
1.59mm |
|
120 |
sec |
| 机械性能 |
洛氏硬度 |
|
ASTM D-785 |
70 |
|
| 拉伸模量 |
|
ASTM D-638 |
2400 |
MPa |
| 拉伸屈服强度 |
|
ASTM D-638 |
60 |
MPa |
| 拉伸断裂强度 |
|
ASTM D-638 |
70 |
MPa |
| 屈服伸长率 |
|
ASTM D-638 |
7 |
% |
| 断裂伸长率 |
|
ASTM D-638 |
100 |
% |
| 弯曲模量 |
|
ASTM D-790 |
2400 |
MPa |
| 弯曲强度 |
屈服 |
ASTM D-790 |
95 |
MPa |
| 悬臂梁缺口冲击强度 |
23℃，3.2mm |
ASTM D-256 |
700 |
J/m |
| 热性能 |
维卡软化点 |
nan |
ISO 306:1994 |
101 |
℃ |
| 热变形温度 |
1.80Mpa |
ISO 75-2:1993 |
90 |
℃ |
| 阻燃等级 |
nan |
UL94 |
HB |
calss |
| 物理性能 |
比重 |
|
ASTM D-792 |
1.2 |
g/cm3 |
| 熔流率 |
300℃/1.2kg |
ASTM D-1238 |
7.0 |
g/10min |
| 收缩率 |
流动 |
ASTM D-955 |
0.5-0.7 |
% |
| 吸水率 |
24hr |
|
0.15 |
% |
| 吸水率 |
饱和 |
|
0.35 |
% |