规格用途
| 规格级别 |
其它 电线电缆料 其它 |
外观颜色 |
nan |
| 该料用途 |
有阻燃要求的船用电缆的绝缘层 |
| 备注说明 |
nan |
技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| |
抗张强度 |
屈服 |
ASTM D638 |
30.4 |
MPa |
| |
断裂 |
ASTM D638 |
37.3 |
MPa |
| 伸长率 |
断裂 |
ASTM D638 |
1000 |
% |
| 拉伸冲击强度 |
|
ASTM D1822 |
343 |
kJ/m² |
| 吸水率 |
|
ASTM D570 |
0.01 |
% |
| 成型收缩率 |
|
ASTM D955 |
0.4-0.6 |
% |
| 断裂伸长率 |
|
ASTM D638 |
35 |
% |
| 弯曲强度 |
|
ASTM D790 |
85 |
MPa |
| 弯曲模量 |
|
ASTM D790 |
2600 |
MPa |
| 简支梁冲击强度 |
缺口,23℃ |
ASTM D256 |
52 |
KJ/m2 |
| |
非缺口,23℃ |
ASTM D256 |
NB |
KJ/m2 |
| 0.45MPa |
|
ASTM D648 |
110 |
℃ |
| 体积电阻率 |
|
ASTM D257 |
1014 |
Ω.m |
| 介电常数 |
1MHz |
ASTM D150 |
|
|
| 损耗因子 |
1MHz |
ASTM D150 |
|
|
| 介电强度 |
2.0 mm厚 |
ASTM D257 |
|
MV/m |
| 基本性能 |
密度 |
|
ASTM D-1505 |
0.958 |
g/cm3 |
| 熔体流动速率 |
MI2.16 |
ASTM D-1238 |
0.25 |
g/10min |
| 热性能 |
熔点 |
|
FPC方法 |
134 |
℃ |
| 脆化温度 |
|
ASTM D-746 |
<-70 |
℃ |
| 软化点 |
|
ASTM D-1525 |
127 |
℃ |
| 玻璃转化温度 |
|
Internal Method |
-46.0 |
℃ |
| 维卡软化温度 |
|
ASTM D1525 |
63.0 |
℃ |
| 溶融温度 |
|
Internal Method |
77.0 |
℃ |
| 结晶峰温 |
|
Internal Method |
60.0 |
℃ |
| 热变形温度 |
0.45MPa，未退火 |
ASTM D-648 |
95.0 |
℃ |
| 热变形温度 |
1.80MPa，未退火 |
ASTM D-648 |
79.4 |
℃ |
| 玻璃转化温度 |
|
Internal Method |
-46.0 |
℃ |
| 维卡软化温度 |
|
ASTM D1525 |
63.0 |
℃ |
| 溶融温度 |
DSC |
Internal Method |
77.0 |
℃ |
| 结晶峰温 |
DSC |
Internal Method |
60.0 |
℃ |
| 其他 |
UL阻燃等级 |
1.6mm |
UL94 |
HB |
|