品名： PP 牌号：4 厂家：利安德巴塞尔
规格用途| 规格级别 | 其它 其它 其它 | 外观颜色 | nan |
| 该料用途 | nan | ||
| 备注说明 | 粘附特点良好 流量高 热密封好， 毒性无 | ||
技术参数| 项目性能 | 性能子项 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|---|
| 基本性能 | 密度 | Method A | ISO 1183 | 0.9 | G/cm3 |
| 熔体流动速率 | 230°C/2.16 kg | ISO 1133 | 13 | g/10min | |
| 密度 | nan | ISO 1183 | 1.20 | g/cm3 | |
| 熔体流动速率 | 220℃,10kg | ISO 1133 | 64 | g/10min | |
| 吸水率 | 23℃,24hr | ISO 62 | 0.30 | % | |
| 比重 | nan | ASTM D-792 | 1.41 | g/cm3 | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 20 | g/10min | |
| 比重 | nan | ASTM D-792 | 0.948 | g/cm3 | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 20 | g/10min | |
| 比重 | nan | ASTM D-792 | 1.33 | g/cm3 | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 20 | g/10min | |
| 比重 | nan | ASTM D-792 | 1.43 | g/cm3 | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 20 | g/10min | |
| 比重 | nan | ASTM D-792 | 1.43 | g/cm3 | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 20 | g/10min | |
| 比重 | nan | ASTM D-792 | 1.38 | g/cm3 | |
| 熔体流动速率 | nan | ASTM D-1238 | 20 | g/10min | |
| 比重 | nan | ASTM D-792 | 1.4 | g/cm3 | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 20 | g/10min | |
| 比重 | nan | ASTM D-792 | 1.35 | g/cm3 | |
| 熔体流动速率 | nan | ASTM D-1238 | 20 | g/10min | |
| 比重 | nan | ASTM D-792 | 1.38 | g/cm3 | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 20 | g/10min | |
| 密度 | nan | ASTM D-792 | 1.15 | g/cm3 | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 20 | g/10min | |
| 密度 | nan | ASTM D-792 | 1.2 | g/cm3 | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 20 | g/10min | |
| 比重 | nan | ASTM D-792 | 1.44 | g/cm3 | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 20 | g/10min | |
| 比重 | nan | ASTM D-792 | 1.39 | g/cm3 | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 12 | g/10min | |
| 比重 | nan | ASTM D-792 | 1.45 | g/cm3 | |
| 熔体流动速率 | nan | ASTM D-1238 | 20 | g/10min | |
| 比重 | nan | ASTM D-792 | 1.75 | g/cm3 | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 20 | g/10min | |
| 热性能 | 维卡软化温度 | A (10N) | ISO 306 | 98 | ℃ |
| 热变形温度 | 1.80MPa，未退火 | ISO 75A-1,-2 | 75.0 | ℃ | |
| 维卡软化温度 | nan | ISO 306 | 86.0 | ℃ | |
| 燃烧性 | 1.50mm | UL 94 | V-0 | nan | |
| 热变形温度 | 0.45 MPa, 未退火 | ISO 75-2/B | 73.0 | ℃ | |
| 维卡软化点 | ISO 306/A50 | 118 | ℃ | ||
| 热变形温度 | 0.45 MPa, 未退火 | ASTM D648 | 110 | ℃ | |
| 热变形温度 | 1.8 MPa, 未退火 | ASTM D648 | 57.0 | ℃ | |
| 线形膨胀系数 - 流动 | ASTM D696 | 0.000090 | cm/cm/℃ | ||
| 热变形温度 | 0.45 MPa, 未退火, 6.00 mm | ASTM D648 | 133 | ℃ | |
| 线形膨胀系数 - 流动 | ASTM D696 | 0.000060 | cm/cm/℃ | ||
| 热稳定性 | CEI 20-34/3-2 | 55.0 | min | ||
| 热 变形温度 | 0.45 MPa, 未退火 | ISO 75-2/B | 190 | °C | |
| 1.8 MPa, 未退火 | ISO 75-2/A | 65.0 | °C | ||
| 维 卡软化温度 | ISO 306/B50 | 195 | °C | ||
| 线 形膨胀系数 | 流 动 (30 到 100°C) | ASTM D696 | 0.00011 | cm/cm/°C | |
| Continuous Use Temperature | 20000 hr | 120 | °C | ||
| 冷挠曲性 | ISO 458 | -24 | ℃ | ||
| 热稳定性 | CEI 20-34/3-2 | 30.0 | min | ||
| 热稳定性 | CEI 20-34/3-2 | > 4 | hr | ||
| 热变形温 度 | 1.8 MPa, 未退火 | ISO 75- 2/Af | 210 | -- | |
| 熔融温度 | ISO 11357-3 | 222 | -- | ||
| 结晶峰温 | ISO 11357-3 | 190 | -- | ||
| 线形膨胀系数 - 流动 | 23 到 85℃ | ISO 11359-2 | 0.000032 | -- | |
| 热变形温 度 | 0.45 MPa, 未退火 | ISO 75-2/B | 210 | -- | |
| 1.8 MPa, 未退火 | ISO 75-2/A | 208 | -- | ||
| 熔融温度 | ASTM D3418 | 220 | -- |