| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
透光量, 0.100" |
nan |
ASTM D-1003 |
88.0 |
% |
| 雾度, 0.100" |
nan |
ASTM D-1003 |
1.0 |
% |
| 折射指数 |
nan |
ASTM D-542 |
1.586 |
nan |
| 电气性能 |
体积电阻率 |
|
ASTM D-257 |
1.0E+17 |
ohm·cm |
| 介电强度 |
|
ASTM D-149 |
15 |
kV/mm |
| 介电常数 |
50Hz |
ASTM D-150 |
3.0 |
|
| 介电常数 |
1MHz |
ASTM D-150 |
2.9 |
|
| 耗散因素 |
50Hz |
ASTM D-150 |
0.00090 |
|
| 耗散因素 |
1MHz |
ASTM D-150 |
0.010 |
|
| 耐电弧性 |
1.59mm |
|
120 |
sec |
| 机械性能 |
洛氏硬度 |
|
ASTM D-785 |
70 |
|
| 拉伸模量 |
|
ASTM D-638 |
2400 |
MPa |
| 拉伸屈服强度 |
|
ASTM D-638 |
60 |
MPa |
| 拉伸断裂强度 |
|
ASTM D-638 |
70 |
MPa |
| 屈服伸长率 |
|
ASTM D-638 |
7 |
% |
| 断裂伸长率 |
|
ASTM D-638 |
100 |
% |
| 弯曲模量 |
|
ASTM D-790 |
2400 |
MPa |
| 弯曲强度 |
屈服 |
ASTM D-790 |
95 |
MPa |
| 悬臂梁缺口冲击强度 |
23℃，3.2mm |
ASTM D-256 |
700 |
J/m |
| 热性能 |
HDT（热畸变温度）, 66 psi, 0.250", 未退火 |
nan |
ASTM D-648 |
280 |
deg F |
| HDT（热畸变温度）, 264 psi, 0.250",未退火 |
nan |
ASTM D-648 |
270 |
deg F |
| 脆性温度 |
nan |
ASTM D-746 |
-200 |
deg F |
| 热指数，机械冲击性能 |
nan |
UL 746B |
100 |
deg C |
| 导热率 |
nan |
ASTM C-177 |
0.19 |
W/m-C |
| 维卡软化温度, B级 |
nan |
ASTM D-1525 |
310 |
deg F |
| CTE（热膨胀系数）, flow, -40F ~ 200F |
nan |
ASTM E-83 |
3 E-5 |
1in/in-F |
| 热指数，非机械冲击性能 |
nan |
UL 746B |
100 |
deg C |
| 比热 |
nan |
ASTM C-351 |
0.30 |
BTU/lb-F |
| 热指数，电性能 |
nan |
UL 746B |
100 |
deg C |
| 热变形温度 |
0.45MPa，未退火 |
ASTM D-648 |
104 |
℃ |
| 热变形温度 |
1.80MPa，未退火 |
ASTM D-648 |
93.9 |
℃ |
| 热变形温度 |
0.45 MPa, 未退火 |
ASTM D648 |
191 |
℃ |
| 热变形温度 |
1.8 MPa, 未退火 |
ASTM D648 |
93.3 |
℃ |
| 熔融温度 |
|
DSC |
216 |
℃ |
| 线形膨胀系数 - 流动 |
|
ASTM D696 |
0.000062 |
cm/cm/℃ |
| 阻燃等级 |
0.810 mm |
UL 94 |
V-2 |
|
| 极限氧指数 |
|
ASTM D2863 |
25 |
% |
| FMVSS 可燃性 |
|
FMVSS 302 |
合格 |
|
| 物理性能 |
比重 |
|
ASTM D-792 |
1.2 |
g/cm3 |
| 熔流率 |
300℃/1.2kg |
ASTM D-1238 |
12 |
g/10min |
| 收缩率 |
流动 |
ASTM D-955 |
0.5-0.7 |
% |
| 吸水率 |
24hr |
|
0.15 |
% |
| 吸水率 |
饱和 |
|
0.35 |
% |