规格用途
| 规格级别 |
增强 其它 其它 |
外观颜色 |
nan |
| 该料用途 |
nan |
| 备注说明 |
30%GF,13%PTFE |
技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTM D-792 |
1.49 |
|
| 比重 |
|
ISO 1183 |
1490 |
|
| 收缩率 |
3.18mm |
ASTM D-955 |
0.20 |
|
| 吸水率 |
24hr |
ASTM D-570 |
0.50 |
|
| 吸水率 |
饱和 |
ISO 62 |
5.3 |
|
| 吸水率 |
平衡 |
ISO 62 |
1.4 |
|
| 热性能 |
热变形温度 |
264psi |
ASTM D648 |
490 |
℉ |
| 阻燃性 |
nan |
UL94 |
HB |
nan |
| 热变形温度 |
1.8MPa,未退火 |
ASTM D-648 |
246 |
℃ |
| 热变形温度 |
0.45MPa,未退火 |
ASTM D-648 |
257 |
℃ |
| 热变形温度 |
1.8MPa,未退火 |
ASTM D-648 |
250 |
℃ |
| 线形膨胀系数 |
流动 |
ASTM D-696 |
0.000023 |
cm/cm/℃ |
| UL阻燃等级 |
|
UL 94 |
HB |
|
| 热变形温度 |
0.45MPa,未退火 |
ASTM D-648 |
260 |
℃ |
| 热变形温度 |
1.8MPa,未退火 |
ASTM D-648 |
252 |
℃ |
| 线形膨胀系数 |
流动 |
ASTM D-696 |
0.000014 |
cm/cm/℃ |
| UL阻燃等级 |
|
UL 94 |
HB |
|
| 热变形温度 |
1.8MPa,未退火 |
ASTM D-648 |
254 |
℃ |
| 线形膨胀系数 |
流动 |
ASTM D-696 |
0.000043 |
cm/cm/℃ |
| UL 阻燃等级 |
1.59mm |
UL 94 |
HB |
|
| 热变形温度 |
0.45MPa |
ISO 75-2 |
260 |
|
| 热变形温度 |
1.8MPa，未退火 |
ASTM D-648 |
254 |
|
| 热变形温度 |
1.8MPa |
ISO 75-2 |
250 |
|
| 溶融温度 |
|
ISO 311357-3 |
260 |
|
| 线膨胀系数 |
流动 |
ASTM D-696 |
0.000043 |
|
| UL 阻燃等级 |
1.59mm |
UL 94 |
HB |
|
| 燃烧性能 |
正常厚度，1.6mm(1.50mm，UL) |
ISO 1210 |
HB |
|
| 热变形温度 |
1.8MPa，未退火 |
ASTM D-648 |
254 |
℃ |
| 线形膨胀系数 |
流动 |
ASTM D-696 |
0.000043 |
cm/cm/℃ |
| UL阻燃等级 |
1.59mm |
UL 94 |
HB |
|
| 热变形温度 |
1.8MPa，未退火 |
ASTM D-648 |
254 |
℃ |
| 线形膨胀系数 |
流动 |
ASTM D-696 |
0.000043 |
cm/cm/℃ |
| UL阻燃等级 |
1.59mm |
UL 94 |
HB |
|
| 热变形温度 |
1.8MPa，未退火 |
ASTM D-648 |
254 |
℃ |
| 线形膨胀系数 |
流动 |
ASTM D-696 |
0.000043 |
cm/cm/℃ |
| UL阻燃等级 |
1.59mm |
UL 94 |
HB |
|
| 热变形温度 |
1.8MPa，未退火 |
ASTM D-648 |
254 |
℃ |
| 线形膨胀系数 |
流动 |
ASTM D-696 |
0.000043 |
cm/cm/℃ |
| UL阻燃等级 |
1.59mm |
UL 94 |
HB |
|
| 热变形温度 |
1.8MPa，未退火 |
ASTM D-648 |
254 |
℃ |
| 线形膨胀系数 |
流动 |
ASTM D-696 |
0.000043 |
cm/cm/℃ |
| UL阻燃等级 |
1.59mm |
UL 94 |
HB |
|
| 热变形温度 |
0.45MPa，未退火 |
ASTM D-648 |
260 |
℃ |
| 热变形温度 |
1.8MPa，未退火 |
ASTM D-648 |
254 |
℃ |
| 热变形温度 |
1.8MPa，未退火 |
ASTM D-648 |
246 |
℃ |
| 热变形温度 |
1.8MPa，未退火 |
ASTM D-648 |
246 |
℃ |
| 线形膨胀系数 |
流动 |
ASTM D-696 |
0.000027 |
cm/cm/℃ |
| 热变形温度 |
|
ASTM D-648 |
250 |
℃ |
| 线形膨胀系数 |
流动 |
ASTM D-696 |
0.000027 |
cm/cm/℃ |