品名： PEI 牌号：2110 厂家：沙伯基础（原GE）
规格用途| 规格级别 | 其它 其它 其它 | 外观颜色 | nan |
| 该料用途 | nan | ||
| 备注说明 | nan | ||
技术参数| 项目性能 | 性能子项 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|---|
| 热性能 | 脆化温度 | ASTM D746 | -70.0 | °C | |
| 维卡软化温度 | ASTM D1525 | 93.0 | °C | ||
| 熔融温度 | ASTM D1525 | 121 | °C | ||
| 基本性能 | 熔体流动速率 | ASTM D-1238 | 12.0 | g/10min | |
| 熔体流动速率 | nan | ASTM D-1238 | 1.0 | g/10min | |
| 密度 | nan | ASTM D-1505 | 0.918 | g/cm3 | |
| 比重 | nan | ASTM D-792 | 1.42 | nan | |
| 密度 | nan | ISO 1183 | 1.08 | g/cm3 | |
| 熔体流动速率 | 220℃/10.0kg | ISO 1133 | 10.0 | cm3/10min | |
| 薄膜 | 薄膜厚度 | 经测试 | 38 | µm | |
| 割线模量 | 1% 正割, MD: 38 µm, 吹塑薄膜 | ASTM D882 | 157 | MPa | |
| 1% 正割, TD: 38 µm, 吹塑薄膜 | ASTM D882 | 196 | MPa | ||
| 抗张强度 | MD: 屈服, 38 µm, 吹塑薄膜 | ASTM D882 | 9.81 | MPa | |
| TD: 屈服, 38 µm, 吹塑薄膜 | ASTM D882 | 10.8 | MPa | ||
| MD: 断裂, 38 µm, 吹塑薄膜 | ASTM D882 | 49.0 | MPa | ||
| TD: 断裂, 38 µm, 吹塑薄膜 | ASTM D882 | 44.1 | MPa | ||
| 伸长率 | MD: 断裂, 38 µm, 吹塑薄膜 | ASTM D882 | 620 | % | |
| TD: 断裂, 38 µm, 吹塑薄膜 | ASTM D882 | 810 | % | ||
| 落锤冲击 | 38 µm, 吹塑薄膜 | ASTM D1709 | 610 | g | |
| 埃尔曼多夫抗撕强度 | MD: 38 µm, 吹塑薄膜 | ASTM D1922 | 460 | g | |
| TD: 38 µm, 吹塑薄膜 | ASTM D1922 | 760 | g | ||
| 热性能 | 燃烧性 | UL 94 | V-0 | class | |
| 热变形温度 | 264Psi | ASTM D-648 | 405 | ℉ | |
| 热指数 | 电性能 | UL746B | 170 | ||
| 热指数 | 机械冲击性能 | UL746B | 170 | ||
| 热指数 | 非机械性能 | UL746B | 170 | ||
| 软化点 | nan | ASTM D-1525 | 93 | ℃ | |
| 熔点 | nan | DSC | 121 | ℃ | |
| 脆化温度 | nan | ASTM D-746 | <-70 | ℃ | |
| 热变形温度 | 1.80MPa，未退火，60.0mmSpan | ISO 75-2/A | 98.0 | ℃ | |
| 维卡软化温度 | nan | ISO 306/B50 | 106 | ℃ |