| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 机械性能 |
硬度计硬度 |
邵氏 A, 1 秒 |
ASTM D2240 |
47 |
|
| 拉伸应力 |
横向流量 (300%应变, 0.889 mm) |
ASTM D412 |
3.10 |
MPa |
| 抗张强度 |
横向流量 (屈服, 0.889 mm) |
ASTM D412 |
19.3 |
MPa |
| 伸长率 |
横向流量 (断裂, 0.889 mm) |
ASTM D412 |
1300 |
% |
| 应力松弛 |
Peak Force @ 200% strain (A): 23℃, 889.0 µm |
|
1.21 |
MPa |
| 应力松弛 |
Peak Force @ 500% strain: 23℃, 889.0 µm |
|
4.07 |
MPa |
| 应力松弛 |
Ratio (A:B): 23℃, 889.0 µm |
|
2.40 |
|
| 应力松弛 |
Relaxation @ 200% strain: 23℃, 889.0 µm |
|
13 |
% |
| 应力松弛 |
Set after 500% strain: 23℃, 889.0 µm |
|
13 |
% |
| 应力松弛 |
Unload @ 50% strain (B): 23℃ 889.0 µm |
|
0.517 |
MPa |
| 补充信息 |
Diblock Content |
|
Internal Method |
< 1.0 |
wt% |
| Mineral Oil Content |
|
Internal Method |
33.0 |
wt% |
| 挥发性 |
|
Internal Method |
0.3 |
wt% |
| 物理性能 |
比重 |
|
ASTM D792 |
0.900 |
g/cm3 |
| 熔流率 |
200℃/5.0kg |
ASTM D1238 |
1.8 |
g/10 min |
| Styrene Content |
|
Internal Method |
31.0 |
wt% |
| 灰含量 |
|
ASTM D1416 |
0.6 |
wt% |